GB 18242-2008 《弹性体改性沥青防水卷材》
GB 18242-2008 Styrene butadiene styrene (SBS) modified bituminous sheet materials
GB 55030-2022 《建筑与市政防水通用规范》
GB 55030-2022 General code for waterproofing of building and municipal engineering
搜索
产品中心
PRODUCTS
+
NRF-M501
弹性体SBS改性沥青防水卷材Modified bituminous waterproof sheet materials
执行标准:
本产品是以苯乙烯-丁二烯-苯乙烯（SBS）嵌段共聚物改性沥青作为涂覆层，并将改性沥青涂盖于聚酯胎基，表面覆以聚乙烯膜（PE）、细砂（S）、矿物粒料（M）所制成的片状防水卷材。
The product is a kind of flexible sheet waterproof material using styrene-butadiene-styrene (SBS) modified bitumen as dipping and coating material, and the reinforcement layer is based on polyester felt, with the surface covered by isolation materials, such as polyethylene film, fine sand, mineral slice (or particle), etc.
执行标准:
GB 18242-2008 《弹性体改性沥青防水卷材》
GB 18242-2008 Styrene butadiene styrene (SBS) modified bituminous sheet materials
GB 55030-2022 《建筑与市政防水通用规范》
GB 55030-2022 General code for waterproofing of building and municipal engineering
产品特点
1、抗拉强度高、延伸率大，可以有效适应基层的收缩变形和开裂；
1. High tensile strength, high elongation, good adaptability to shrinkage deformation and cracking of the substratum.
1. High tensile strength, high elongation, good adaptability to shrinkage deformation and cracking of the substratum.
2、良好的高低温性能，可在-20℃环境下施工，适用于高低温地区，尤其适用于寒冷区域。
2. Good temperature resistance: can be applied under -20℃, suitable for cold and hot regions, especially for cold area.
3、矿物粒料类卷材耐老化性、抗紫外线性能优异；
3. Product surface with mineral particle isolation material has excellent ageing resistance and anti-ultraviolet performance.
4、以聚酯胎基作为增强层，有效提升防水层的机械强度、耐穿刺、耐撕裂等性能；
4. The polyester reinforcement promotes mechanical strength, root penetration resistance and Tear resistance, etc.
5、热熔施工，火烤易出油，工法成熟，防水效果可靠。
5. Good workability: can be applied by torch-applied method in any season and hot-joint makes the work reliable and durable.
产品规格
|
项目 |
标准要求 |
|
产品型号 |
Ⅰ型，Ⅱ型 |
|
卷材长度 |
7.5m，710m |
|
卷材宽度 |
1m |
|
卷材厚度 |
3mm，4mm |
|
卷材面积 |
7.5㎡，10㎡ |
|
上表面隔离材料 |
聚乙烯膜（PE），细砂（S），矿物粒料（M） |
|
下表面隔离材料 |
聚乙烯膜（PE） |
性能指标
|
序号 |
项目 |
指标 |
|||
|
Ⅰ |
Ⅱ |
||||
|
1 |
可溶物含量/(g/㎡) ≥ |
3㎜ |
2100 |
||
|
4㎜ |
2900 |
||||
|
5㎜ |
3500 |
||||
|
2 |
耐热性 |
℃ |
90 |
105 |
|
|
≦㎜ |
2 |
||||
|
实验现象 |
无流淌、滴落 |
||||
|
3 |
低温柔性/℃ |
-20℃ |
-25℃ |
||
|
无裂缝 |
|||||
|
4 |
不透水性/30min |
0.3MPa不透水 |
|||
|
5 |
最大峰拉力(N/50㎜) ≥ |
纵向 |
500 |
800 |
|
|
横向 |
|||||
|
6 |
最大峰时延伸率/% ≥ |
纵向 |
30 |
40 |
|
|
横向 |
|||||
适用范围
适用于工业、民用及市政建设的屋面和地下防水工程。
Waterproofing for various roof and underground engineering of industrial, civil and municipal construction projects.
贮存运输
1．不同类型、规格的产品应分别存放，不应混杂；
2．避免日晒雨淋，注意通风，贮存温度不应高于50℃；
3．立放贮存只能单层，运输过程中立放不超过两层；
4．运输时防止倾斜或横压，必要时加盖苫布；
5．在正常贮存和运输条件下，贮存期自生产日起为一年。
2．避免日晒雨淋，注意通风，贮存温度不应高于50℃；
3．立放贮存只能单层，运输过程中立放不超过两层；
4．运输时防止倾斜或横压，必要时加盖苫布；
5．在正常贮存和运输条件下，贮存期自生产日起为一年。